  <dc:creator>Peutzfeldt A</dc:creator>
  <dc:creator>Sahafi A</dc:creator>
  <dc:creator>Flury S</dc:creator>
  <dc:date>2011</dc:date>
  <dc:description xmlns:ns0="xml" ns0:lang="en">The aim was to compare eight types of luting agents when used to bond six indirect, laboratory restorative materials to dentin. Cylinders of the six restorative materials (Esteticor Avenir [gold alloy], Tritan [titanium], NobelRondo [feldspathic porcelain], Finesse All-Ceramic [leucite-glass ceramic], Lava [zirconia], and Sinfony [resin composite]) were ground and air-abraded. Cylinders of feldspathic porcelain and glass ceramic were additionally etched with hydrofluoric acid and were silane-treated. The cylinders were luted to ground human dentin with eight luting agents (DeTrey Zinc [zinc phosphate cement], Fuji I [conventional glass ionomer cement], Fuji Plus [resin-modified glass ionomer cement], Variolink II [conventional etch-and-rinse resin cement], Panavia F2.0 and Multilink [self-etch resin cements], and RelyX Unicem Aplicap and Maxcem [self-adhesive resin cements]). After water storage at 37°C for one week, the shear bond strength of the specimens (n=8/group) was measured, and the fracture mode was stereomicroscopically examined. Bond strength data were analyzed with two-factorial analysis of variance (ANOVA) followed by Newman-Keuls' Multiple Range Test (α=0.05). Both the restorative material and the luting agent had a significant effect on bond strength, and significant interaction was noted between the two variables. Zinc phosphate cement and glass ionomer cements produced the lowest bond strengths, whereas the highest bond strengths were found with the two self-etch and one of the self-adhesive resin cements. Generally, the fracture mode varied markedly with the restorative material. The luting agents had a bigger influence on bond strength between restorative materials and dentin than was seen with the restorative material.</dc:description>
  <dc:format>application/pdf</dc:format>
  <dc:identifier>https://sonar.ch/global/documents/162623</dc:identifier>
  <dc:language>eng</dc:language>
  <dc:relation>info:eu-repo/semantics/altIdentifier/doi/10.2341/10-236-L</dc:relation>
  <dc:relation>info:eu-repo/semantics/altIdentifier/pmid/21740244</dc:relation>
  <dc:rights>info:eu-repo/semantics/openAccess</dc:rights>
  <dc:source>Operative dentistry. - 2011</dc:source>
  <dc:subject xmlns:ns1="xml" ns1:lang="en">Acid Etching, Dental</dc:subject>
  <dc:subject xmlns:ns2="xml" ns2:lang="en">Aluminum Oxide</dc:subject>
  <dc:subject xmlns:ns3="xml" ns3:lang="en">Aluminum Silicates</dc:subject>
  <dc:subject xmlns:ns4="xml" ns4:lang="en">Carbon Compounds, Inorganic</dc:subject>
  <dc:subject xmlns:ns5="xml" ns5:lang="en">Cementation</dc:subject>
  <dc:subject xmlns:ns6="xml" ns6:lang="en">Ceramics</dc:subject>
  <dc:subject xmlns:ns7="xml" ns7:lang="en">Composite Resins</dc:subject>
  <dc:subject xmlns:ns8="xml" ns8:lang="en">Dental Bonding</dc:subject>
  <dc:subject xmlns:ns9="xml" ns9:lang="en">Dental Cements</dc:subject>
  <dc:subject xmlns:ns10="xml" ns10:lang="en">Dental Etching</dc:subject>
  <dc:subject xmlns:ns11="xml" ns11:lang="en">Dental Materials</dc:subject>
  <dc:subject xmlns:ns12="xml" ns12:lang="en">Dental Porcelain</dc:subject>
  <dc:subject xmlns:ns13="xml" ns13:lang="en">Dental Restoration, Permanent</dc:subject>
  <dc:subject xmlns:ns14="xml" ns14:lang="en">Dentin</dc:subject>
  <dc:subject xmlns:ns15="xml" ns15:lang="en">Dentin-Bonding Agents</dc:subject>
  <dc:subject xmlns:ns16="xml" ns16:lang="en">Glass Ionomer Cements</dc:subject>
  <dc:subject xmlns:ns17="xml" ns17:lang="en">Gold Alloys</dc:subject>
  <dc:subject xmlns:ns18="xml" ns18:lang="en">Humans</dc:subject>
  <dc:subject xmlns:ns19="xml" ns19:lang="en">Hydrofluoric Acid</dc:subject>
  <dc:subject xmlns:ns20="xml" ns20:lang="en">Materials Testing</dc:subject>
  <dc:subject xmlns:ns21="xml" ns21:lang="en">Potassium Compounds</dc:subject>
  <dc:subject xmlns:ns22="xml" ns22:lang="en">Resin Cements</dc:subject>
  <dc:subject xmlns:ns23="xml" ns23:lang="en">Silicon Compounds</dc:subject>
  <dc:subject xmlns:ns24="xml" ns24:lang="en">Stress, Mechanical</dc:subject>
  <dc:subject xmlns:ns25="xml" ns25:lang="en">Surface Properties</dc:subject>
  <dc:subject xmlns:ns26="xml" ns26:lang="en">Titanium</dc:subject>
  <dc:subject xmlns:ns27="xml" ns27:lang="en">Zinc Phosphate Cement</dc:subject>
  <dc:subject xmlns:ns28="xml" ns28:lang="en">Zirconium</dc:subject>
  <dc:title xmlns:ns29="xml" ns29:lang="en">Bonding of restorative materials to dentin with various luting agents.</dc:title>