Corneal biomechanical properties at different corneal cross-linking (CXL) irradiances.
- Hammer A Department of Ophthalmology, Geneva University Hospitals, Geneva, Switzerland.
- Richoz O
- Arba Mosquera S
- Tabibian D
- Hoogewoud F
- Hafezi F
- 2014-03-29
Published in:
- Investigative ophthalmology & visual science. - 2014
biomechanics
corneal cross-linking
efficiency
high irradiance
oxygen
Analysis of Variance
Animals
Biomechanical Phenomena
Collagen
Cornea
Cross-Linking Reagents
Dose-Response Relationship, Radiation
Elasticity
Humans
Models, Animal
Photosensitizing Agents
Riboflavin
Swine
Ultraviolet Rays
English
PURPOSE
New corneal cross-linking (CXL) devices are capable of using higher UV-A light irradiances than used in original CXL protocols. The Bunsen-Roscoe law states that a photochemical reaction should stay constant if the delivered total energy is kept constant; however, little clinical data are available to support this hypothesis.
METHODS
We investigated the biomechanical properties of four groups (n = 50 each) of porcine corneas. Three groups were exposed to riboflavin 0.1 % and UV-A irradiation of equal total energy (3 mW/cm(2) for 30 minutes, 9 mW/cm(2) for 10 minutes, and 18 mW/cm(2) for 5 minutes). Controls were exposed to riboflavin 0.1% without irradiation. Young's modulus of 5-mm wide corneal strips was used as an indicator of corneal stiffness.
RESULTS
We observed a decreased stiffening effect with increasing UV-A intensity. Young's modulus at 10% strain showed significant differences between 3 mW/cm(2) and 9 mW/cm(2) (P = 0.002), 3 mW/cm(2) and 18 mW/cm(2) (P = 0.0002), 3 mW/cm(2) and the control group (P < 0.0001), and 9 mW/cm(2) and the control group (P = 0.015). There was no difference between 18 mW/cm(2) and the control group (P = 0.064) and between 9 mW/cm(2) and 18 mW/cm(2) (P = 0.503).
CONCLUSIONS
The biomechanical effect of CXL decreased significantly when using high irradiance/short irradiation time settings. Intrastromal oxygen diffusion capacity and increased oxygen consumption associated with higher irradiances may be a limiting factor leading to reduced treatment efficiency. Our results regarding the efficiency of high-irradiance collagen cross-linking (CXL) raise concerns about the clinical efficiency of the new high-irradiance CXL devices already used in clinical practice without proper validation.
New corneal cross-linking (CXL) devices are capable of using higher UV-A light irradiances than used in original CXL protocols. The Bunsen-Roscoe law states that a photochemical reaction should stay constant if the delivered total energy is kept constant; however, little clinical data are available to support this hypothesis.
METHODS
We investigated the biomechanical properties of four groups (n = 50 each) of porcine corneas. Three groups were exposed to riboflavin 0.1 % and UV-A irradiation of equal total energy (3 mW/cm(2) for 30 minutes, 9 mW/cm(2) for 10 minutes, and 18 mW/cm(2) for 5 minutes). Controls were exposed to riboflavin 0.1% without irradiation. Young's modulus of 5-mm wide corneal strips was used as an indicator of corneal stiffness.
RESULTS
We observed a decreased stiffening effect with increasing UV-A intensity. Young's modulus at 10% strain showed significant differences between 3 mW/cm(2) and 9 mW/cm(2) (P = 0.002), 3 mW/cm(2) and 18 mW/cm(2) (P = 0.0002), 3 mW/cm(2) and the control group (P < 0.0001), and 9 mW/cm(2) and the control group (P = 0.015). There was no difference between 18 mW/cm(2) and the control group (P = 0.064) and between 9 mW/cm(2) and 18 mW/cm(2) (P = 0.503).
CONCLUSIONS
The biomechanical effect of CXL decreased significantly when using high irradiance/short irradiation time settings. Intrastromal oxygen diffusion capacity and increased oxygen consumption associated with higher irradiances may be a limiting factor leading to reduced treatment efficiency. Our results regarding the efficiency of high-irradiance collagen cross-linking (CXL) raise concerns about the clinical efficiency of the new high-irradiance CXL devices already used in clinical practice without proper validation.
- Language
-
- English
- Open access status
- green
- Identifiers
-
- DOI 10.1167/iovs.13-13748
- PMID 24677109
- Persistent URL
- https://sonar.ch/global/documents/252130
Statistics
Document views: 46
File downloads:
- Full-text: 0